ResinLab EP1340 Epoxy Encapsulant Black 400 mL Cartridge

Part number: EP1340 BLACK 400ML
ResinLab EP1340 Epoxy Encapsulant Black 400 mL Cartridge
Quantity Price
1 $2,083.44 ($86.81 each) 2083.440000000 USD New Limited Availability EP1340 BLACK 400ML
2 $1,604.40 ($66.85 each) 1604.400000000 USD New Limited Availability EP1340 BLACK 400ML
3+ $1,489.68 ($62.07 each) 1489.680000000 USD New Limited Availability EP1340 BLACK 400ML
Sold as a pack (24/pk).
Usually Ships in 2-3 Business Days. Non-returnable product. Canceled orders may incur a fee at the supplier’s discretion.

ResinLab EP1340 Black is a two component, room temperature or heat curing, flame resistant epoxy casting system that is used for bonding to most materials and filling voids. It is semi-rigid, free flowing, has good wetting and air release. It is resistant to salt solutions, water, organic and inorganic solvents. 400 mL Cartridge.

<p>ResinLab EP1340 Black is a two component, room temperature or heat curing, flame resistant epoxy casting system that is used for bonding to most materials and filling voids. It is semi-rigid, free flowing, has good wetting and air release. It is resistant to salt solutions, water, organic and inorganic solvents. 400 mL Cartridge.</p>
Typical Use: It has good wetting and adhesion to most surfaces and is free flowing to penetrate voids and give good air release.
Chemical Composition: Epoxy
Color: Black
Components: 2 part
Cure System: Room Temperature/Heat
Cure Time: 24 to 48h @ 25 °C; 2h @ 60 °C; 30min @ 100 °C
Dielectric Strength: 513 V/mil
Elongation: 9%
Flash Point: >93 °C
Hardness: 85 D
Mix Ratio: 1:1 by volume; 1.11:1 by weight
Service Temperature: -40 to 150 °C
Shear Strength: 1,300
Specific Gravity: Part A: 1.37; Part B: 1.23; Mixed: 1.30
Tensile Strength: 1,300 psi
Thermal Conductivity: 0.22 W/mK
Viscosity: Part A: 12,000; Part B: 16,000; Mixed: 13,500
Volume Resistivity: 1.51 x 10^14 ohm-cm

 